L605 Round Bar
These bars’ excellent properties and features make them ideal for gas turbine applications, liners, combustion chamber components, and jet engine parts.
UDIMET L605 Round Bars have excellent corrosion resistance in the hot corrosive sections and working surroundings. This alloy or metal comes with the high chromium content. Hence, they are resistant to corrosion in many applications that contain liquid formats such as acidic environments.
Heat treatments details of UDIMET L605 Round Bars:
UDIMET L605 Round Bars contains the higher strength than achieved in L 605 by work hardening. L 605 remains a non-magnetic alloy after being work hardened. That’s why L 605 is typically used in cold-worked conditions. This has decent increase feature in hardness and strength can be achieved by aging the cold-worked material.
Udimet L605 Round Bars Specification
Specification : AMS 5759, ASTM F90
Standard : EN, DIN, JIS, ASTM, BS, ASME, AISI
Round Bars : Outside Diameter in the range of 4mm to 500mm
Bright Bars : Outside Diameter in the range of 4mm to 100mm
Hex Bars : 18mm – 57mm (11/16″ to 2-3/4″)
Square Bars : 18mm – 47mm (11/16″ to 1-3/4″)
Finish : Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish
Length : 1 to 6 Meters, Custom Cut Lengths
Form : Round, Square, Hex (A/F), Rectangle Etc.
Buy Huge Quantity of L605 Alloy Bars, Alloy L605 Bar Manufacturer, Nickel Alloy L-605 Hex Bar, UNS R30605 Round Rod Exporter, Udimet L605 Square Bar, Cobalt Alloy L605 Industrial Bars, UNS R30605 Flat Bars, L605 Bar Stock, Udimet Alloy L605 Bar Stockist in India.
Common applications where UDIMET L605 Round Bar:
- Engine combustor liners in aircraft
- Components of the jet engine and aerospace
- Land-based gas turbine combustor liners
- Industrial furnace lines
- Mufflers and liners for high-temperature kilns
- High-temperature ball bearings
- Marine turbines
UDIMET L605 Round Bars are manufactured with the grades used to improve machining the material into parts, grades for great surface finishing and high hardness by responding to heat processes and treatment and grades with qualitative corrosion qualities.
Equivalent Grades of L605 Round Bars
| STANDARD | WERKSTOFF NR. | UNS |
| Alloy L605 | 2.4964 | R30605 |
L605 Round Bar Chemical Composition Chart
| Weight% | C | P | Si | Ni | W | Mn | S | Cr | Co | Fe |
| Alloy L-605 | 0.05 – 0.15 | 0.040 max | 0.40 max | 9.0 – 11.0 | 14.0 – 16.0 | 1.0 – 2.0 | 0.030 max | 19.0 – 21.0 | Bal | 3.0 max |
L605 Alloy Round Bar Mechanical Properties
| Material | Temperature °F | Yield Strength 0.2% | Tensile Strength | Elongation (%) | Hardness HB |
| Extruded Bar L-605 | RT | 310 Mpa 45 KSI | 862 Mpa 125 KSI | 30 | 277 max |